Poly(allylamine) is one of the cationic polymer. In SEC analysis of cationic polymer, the selection of eluent which prevents ionic interaction and hydrophobic interaction between a sample and gel makes measurement successful. In order to control the ionic interaction between a sample and gel, salt should beadded to the eluent. But if the salt containing multivalent anion such as phosphate or sulfate is used, a sample may not dissolve or a sample may precipitate after the dissolution. On the other hand, if the salt containing one valent anion such as nitrate and chloride is used, precipitation of a sample will not take place. Here, the influence to the chromatogram of the salt concentration in the eluent was investigated under the various concentration of sodium nitrate in the eluent. In order to reduce hydrophobic interaction between a sample and gel, 0.5 M acetic acid was added to the eluent. Comparison of chromatograms of poly(allylamine) measured under the various concentration of sodium nitrate in the eluent is shown in Fig.1. In the case of 0.02 M sodium nitrate in the eluent, the constituent of high molecular weight of poly(allylamine) is adsorbed to the gel material and is not eluted from a column. When the salt concentration of sodium nitrate is more than 0.1 M, the adsorption of a sample is suppressed and a right chromatogram is obtained. The relation between the molecular weight of poly(allylamine) and elution volume with SEC/MALS is shown in Fig.2. Under the 0.1 M - 0.2 M of sodium nitrate in the eluent, poly(allylamine) is eluted in the molecular weight order. The relation between the RMS radius (size of the molecule in the solution) of poly(allylamine) and elution volume with SEC/MALS is shown in Fig.3. When the concentration of sodium nitrate is low, molecule of the polymer spreads out and RMS radius becomes large, as the result, poly(allylamine) is eluted early. When the salt concentration is 0.1-0.2 M, we can see the influence of the diffusion of molecule is decreasing according to the salt concentration, and separation is performed in the molecular size order. From the above result, in the measurement of poly(allylamine) with SB-806M HQ, the eluent of 0.5 M acetic acid + 0.1 M - 0.2 M sodium nitrate is sutable for this analysis.







Sample : 0.2 % Poly(allylamine), 100 μL

Columns      : Shodex OHpak SB-806M HQ (8.0 mm I.D. x 300 mm) x 2
Eluent       : 0.5 M CH3COOH + n M NaNO3 aq.
Flow rate    : 1.0 mL/min
Detector     : RI, MALS(Multi Angle Light Scattering Detector)
Column temp. : 40 °C